Kinerja Pencampuran Pewarna Kunyit dan Indigofera dengan Molaritas Indigo/Kunyit 0,32M/0,23M sebagai Sensitizer Pada Dye Sensitized Solar Cells (DSSCC)

- Basuki

Abstract

Abstrak
Penelitian ini bertujuan untuk menguji kinerja pencampuran pewarna kunyit dan indigo. Pewarna kunyit diperoleh dengan metode ekstraksi, sedangkan pewarna indigo diperoleh dengan metode fermentasi dari tanaman indigofera. Pewarna indigofera dan kunyit diberi perlakuan pencampuran pewarna dengan molaritas indigo/kunyit 0,32M/0,23M. Karakteristik dari pewarna tersebut dipelajari. Pada pewarna alami dilakukan pengujian absorbansi, FTIR, dan cyclic voltammetry. Pencampuran pewarna tersebut kemudian diaplikasikan pada dye-sensitized solar cells (DSSCs) dan kemudian kinerja DSSC diuji pada 0 jam. Hasil UV-Vis menunjukkan bahwa serapan cahaya pewarna dengan molaritas indigo/kunyit 0,32M/0,23M dengan puncak serapan 375 - 525 nm. Dari pengujian FTIR teridentifikasi gugus fungsi pencampuran pewarna dengan molaritas indigo/kunyit 0,32M/0,23M adalah –OH, cincin aromatik C=C, alkana C-H, amina C-N. Hasil uji cyclic voltammetry menunjukkan bahwa pencampuran pewarna dengan molaritas indigo/kunyit 0,32M/0,23M mempunyai band gap 0,745 eV. Dari penelitian ini efisiensi yang dihasilkan oleh sel surya adalah 0,038%.
Kata Kunci: Pewarna alami, kunyit, indigofera, molaritas, kinerja, sel surya.
Abstract
The research is to examine the performance of solar cell with turmeric and indigo dye. Turmeric dye is obtained by extraction method while the indigo dye is obtained by fermentation method from indigofera plants. Indigofera and turmeric dyes were treated by mixing dye with indigo / turmeric molarity 0.32M / 0.23M. Characteristics of the dye are studied. The natural dye was tested with absorbance test, FTIR and cyclic voltammetry. The dye mixing was then applied to dye-sensitized solar cells (DSSCs) and then DSSC performance was tested at 0 hours. The UV-Vis results showed that the dye absorption with indigo / turmeric molarity was 0.32M / 0.23M with an absorption peak of 375 - 525 nm. From the FTIR test, the dyeing function mixing group with indigo / turmeric molarity of 0.32M / 0.23M is -OH, C = C aromatic, alkane C-H, amina C-N. The result of cyclic voltammetry test showed that mixing dye with indigo / turmeric molarity 0,32M / 0,23M band gap 0,745 eV. Result from this research of solar cell efficiency is 0.038%.
Keywords: Natural dyes, turmeric, indigofera, molarity, performance, solar cells.